CYCOLOY™Resin C6200

SI

|British

|Metric

|PDF

Americas: COMMERCIAL

Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.

Property

MECHANICAL

Tensile Stress, yld, Type I, 50 mm/min

680

kgf/cm2

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

50

%

ASTM D 638

Flexural Stress, yld, 2.6 mm/min, 100 mm span

1050

kgf/cm2

ASTM D 790

Flexural Modulus, 2.6 mm/min, 100 mm span

27400

kgf/cm2

ASTM D 790

IMPACT

Izod Impact, notched, 23°C

54

cm-kgf/cm

ASTM D 256

Instrumented Impact Energy @ peak, 23°C

622

cm-kgf

ASTM D 3763

Instrumented Impact Energy @ peak, -30

553

cm-kgf

ASTM D 3763

THERMAL

HDT, 1.82 MPa, 3.2mm, unannealed

87

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

90

°C

ASTM D 648

Relative Temp Index, Elec

85

°C

UL 746B

Relative Temp Index, Mech w/impact

85

°C

UL 746B

Relative Temp Index, Mech w/o impact

85

°C

UL 746B

PHYSICAL

Specific Gravity

1.18

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.4 - 0.6

%

SABIC Method

Mold Shrinkage, xflow, 3.2 mm (5)

0.4 - 0.6

%

SABIC Method

Melt Flow Rate, 260°C/2.16 kgf

14.5

g/10 min

ASTM D 1238

Spiral Flow,260°C,10 ips,3.175 X 1524 mm

685.8

mm

-

ELECTRICAL

Arc Resistance, Tungsten {PLC}

6

PLC Code

ASTM D 495

Hot Wire Ignition {PLC)

2

PLC Code

UL 746A

High Voltage Arc Track Rate {PLC}

3

PLC Code

UL 746A

High Ampere Arc Ign, surface {PLC}

0

PLC Code

UL 746A

Comparative Tracking Index (UL) {PLC}

2

PLC Code

UL 746A

Volume Resistivity

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity, ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength, in oil, 0.8 mm

35

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 1.6 mm

25

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 3.2 mm

17

kV/mm

IEC 60243-1

Relative Permittivity, 1 MHz

2.7

-

IEC 60250

Dissipation Factor, 50/60 Hz

0.004

-

IEC 60250

Dissipation Factor, 1 MHz

0.008

-

IEC 60250

Relative Permittivity, 50/60 Hz

2.8

-

IEC 60250

FLAME CHARACTERISTICS

UL Recognized, 94HB Flame Class Rating (3)

0.71

mm

UL 94

UL Recognized, 94V-1 Flame Class Rating (3)

1.21

mm

UL 94

UL Recognized, 94V-0 Flame Class Rating (3)

1.47

mm

UL 94

UL Recognized, 94-5VA Rating (3)

3.4

mm

UL 94

UL Recognized, 94-5VB Rating (3)

2

mm

UL 94

Source GMD, last updated:2000/01/05

Processing

Injection Molding

Drying Temperature

80 - 90

°C

Drying Time

3 - 4

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0.04

%

Melt Temperature

245 - 275

°C

Nozzle Temperature

245 - 275

°C

Front - Zone 3 Temperature

245 - 275

°C

Middle - Zone 2 Temperature

220 - 275

°C

Rear - Zone 1 Temperature

220 - 255

°C

Mold Temperature

60 - 80

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

40 - 70

rpm

Shot to Cylinder Size

30 - 80

%

Vent Depth

0.038 - 0.076

mm