CYCOLOY™Resin CP8320

SI

|British

|Metric

|PDF

Americas: COMMERCIAL

Cycoloy Medium Heat Plating Grade for Automotive

Property

MECHANICAL

Tensile Stress, yld, Type I, 50 mm/min

450

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 50 mm/min

400

kgf/cm2

ASTM D 638

Tensile Strain, yld, Type I, 50 mm/min

4

%

ASTM D 638

Tensile Strain, brk, Type I, 50 mm/min

100

%

ASTM D 638

Tensile Modulus, 5 mm/min

21400

kgf/cm2

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

710

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

20300

kgf/cm2

ASTM D 790

Tensile Stress, yield, 50 mm/min

45

MPa

ISO 527

Tensile Stress, break, 50 mm/min

40

MPa

ISO 527

Tensile Strain, yield, 50 mm/min

4

%

ISO 527

Tensile Strain, break, 50 mm/min

100

%

ISO 527

Tensile Modulus, 1 mm/min

2100

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

65

MPa

ISO 178

Flexural Modulus, 2 mm/min

2000

MPa

ISO 178

IMPACT

Izod Impact, notched, 23°C

61

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -30°C

40

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

560

cm-kgf

ASTM D 3763

Izod Impact, notched 80*10*3 +23°C

60

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*3 -30°C

30

kJ/m2

ISO 180/1A

Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm

60

kJ/m2

ISO 179/1eA

Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm

30

kJ/m2

ISO 179/1eA

THERMAL

Vicat Softening Temp, Rate B/50

106

°C

ASTM D 1525

HDT, 1.82 MPa, 3.2mm, unannealed

90

°C

ASTM D 648

CTE, -40°C to 40°C, flow

9.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

9.E-05

1/°C

ASTM E 831

Thermal Conductivity

0.2

W/m-°C

ISO 8302

CTE, -40°C to 40°C, flow

9.E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

9.E-05

1/°C

ISO 11359-2

Ball Pressure Test, 75°C +/- 2°C

Pass

-

IEC 60695-10-2

Vicat Softening Temp, Rate B/50

106

°C

ISO 306

Vicat Softening Temp, Rate B/120

107

°C

ISO 306

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

92

°C

ISO 75/Af

PHYSICAL

Specific Gravity

1.1

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.5 - 0.7

%

SABIC Method

Melt Flow Rate, 260°C/5.0 kgf

14

g/10 min

ASTM D 1238

Density

1.1

g/cm3

ISO 1183

Water Absorption, (23°C/sat)

0.3

%

ISO 62

Moisture Absorption (23°C / 50% RH)

0.1

%

ISO 62

Melt Volume Rate, MVR at 260°C/5.0 kg

13

cm3/10 min

ISO 1133

ELECTRICAL

Volume Resistivity

>1.E+15

Ohm-cm

IEC 60093

Surface Resistivity, ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength, in oil, 0.8 mm

35

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 1.6 mm

25

kV/mm

IEC 60243-1

Dielectric Strength, in oil, 3.2 mm

17

kV/mm

IEC 60243-1

Source GMD, last updated:2006/06/14

Processing

Injection Molding

Drying Temperature

95 - 105

°C

Drying Time

2 - 4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

250 - 280

°C

Nozzle Temperature

230 - 270

°C

Front - Zone 3 Temperature

240 - 280

°C

Middle - Zone 2 Temperature

240 - 280

°C

Rear - Zone 1 Temperature

220 - 250

°C

Hopper Temperature

60 - 80

°C

Mold Temperature

60 - 90

°C