規(guī)格：25KG/BAG
所屬類型：其它原材料
品牌：
型號(hào)：Cycoloy PC/ABS CY9650
性能：通用級(jí)，Cycoloy PC/ABS，熱穩(wěn)定，沖擊改性，穩(wěn)定。
PC+ABS, High IMPACT and High Flow, ductility at low temperature, excellent properties retention after Hydrolytic and Heat Aging
| TYPICAL PROPERTIES(1) | ||||
| MECHANICAL機(jī)械性能 | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min / 抗拉強(qiáng)度,屈服,類型I,50 mm/min | 54 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min / 抗拉強(qiáng)度, 斷裂, 類型I, 50 mm/min | 53 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min / 拉伸伸長, 屈服, 類型I, 50 mm/min | 4.5 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min / 拉伸伸長,斷裂,類型I, 50 mm/min | 120 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min / 拉伸模量,5 mm/min | 2300 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span / 撓曲強(qiáng)度, 屈服, 1.3 mm/min, 50 mm 跨距 | 89 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span / 撓曲模量, 1.3 mm/min, 50 mm 跨距 | 2300 | MPa | ASTM D 790 | |
| Tensile Stress, yield 50 mm/min / 抗張程度，屈服, 50 mm/min | 54 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min / 抗張程度,斷裂,50mm/min | 53 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min / 拉伸伸長,屈服,,50mm/min | 4.5 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min / 拉伸伸長,斷裂,50mm/min | 120 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min / 拉伸模量,1 mm/min | 2250 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min / 彎曲強(qiáng)度,屈服,2 mm/min | 82 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min / 彎曲模量,2 mm/min | 2200 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C / 懸臂梁缺口沖擊強(qiáng)度23°C | 590 | J/m | ASTM D 256 | |
| Izod IMPACT, notched, -30°C / 懸壁梁缺口沖擊強(qiáng)度, -30°C | 430 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C / 儀表控制抗沖擊總能量，23°C | 55 | J | ASTM D 3763 | |
| Instrumented IMPACT Total Energy, -30°C / 裝有測(cè)量儀表的落鏢沖擊Total Energy，-30°C | 67 | J | ASTM D 3763 | |
| Izod IMPACT, notched 80*10*3 +23°C / 懸壁梁缺口沖擊強(qiáng)度, 80*10*3 +23°C | 65 | kJ/m2 | ISO 180/1A | |
| Izod IMPACT, notched 80*10*3 -30°C / 懸壁梁缺口沖擊強(qiáng)度, 80*10*3 -30°C | 30 | kJ/m2 | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm / 簡支梁缺口沖擊強(qiáng)度，23°C，C80*10*3 sp=62mm | 65 | kJ/m2 | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm / 簡支梁缺口沖擊強(qiáng)度，-30°C，C80*10*3 sp=62mm | 30 | kJ/m2 | ISO 179/1eA | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 / 維卡軟化溫度 B級(jí)/50 | 126 | °C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed / 熱變形溫度,1.82 MPa, 3.2mm,未退火 | 107 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow / 線形膨脹系數(shù),-40°C 到40°C,流動(dòng) | 7.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow / 線形膨脹系數(shù),-40°C 到40°C,橫向 | 7.E-05 | 1/°C | ASTM E 831 | |
| Thermal Conductivity / 導(dǎo)熱系數(shù) | 0.2 | W/m-°C | ISO 8302 | |
| CTE, -40°C to 40°C, flow / 線形膨脹系數(shù),-40°C 到40°C,流動(dòng) | 8.E-05 | 1/°C | ISO 11359-2 | |
| CTE, -40°C to 40°C, xflow / 線形膨脹系數(shù),-40°C 到40°C,橫向 | 8.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 75°C +/- 2°C | Pass | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 / 維卡軟化溫度 B級(jí)/50 | 126 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 / 維卡軟化溫度,B級(jí)/120 | 127 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 126 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm / 熱變形溫度，1.8 MPa, 未退火,80*10*4， 64.0 mm 跨距 | 105 | °C | ISO 75/Af | |
| Relative Temp Index, Elec / 相對(duì)熱指數(shù)， 電性能 | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact / 相對(duì)熱指數(shù)，機(jī)械沖擊性能 | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact / 相對(duì)熱指數(shù)，非機(jī)械沖擊性能 | 60 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity/比重 | 1.14 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm / 模塑收縮量，流動(dòng)，3.2 mm | 0.5 - 0.7 | % | SABIC Method | |
| Mold Shrinkage, xflow, 3.2 mm / 模塑收縮量，橫向，3.2 mm | 0.5 - 0.7 | % | SABIC Method | |
| Melt Flow Rate / 熔流率, 260°C/5.0 kgf | 26 | g/10 min | ASTM D 1238 | |
| Density/密度 | 1.14 | g/cm3 | ISO 1183 | |
| Water Absorption, (23°C/sat) / 吸水率, (23°C/sat) | 0.4 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) / 吸水率, 平衡,(23°C / 50% RH) | 0.15 | % | ISO 62 | |
| Melt Volume Rate, MVR at 260°C/5.0 kg / 溶化體積流率,MVR, 260°C/5.0 kg | 25 | cm3/10 min | ISO 1133 | |
| Melt Viscosity, 260°C, 1500 sec-1 / 熔體粘度，260°C, 1500 sec-1 | 170 | Pa-s | ISO 11443 | |
| ELECTRICAL | Value | Unit | Standard | |
| Volume Resistivity/體積電阻率 | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA / 表面電阻率 | >1.E+15 | Ohm | IEC 60093 | |
| Dielectric Strength, in oil, 0.8 mm / 耐電強(qiáng)度，在油中，0.8mm | 35 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 1.6 mm / 耐電強(qiáng)度，在油中，1.6mm | 25 | kV/mm | IEC 60243-1 | |
| Dielectric Strength, in oil, 3.2 mm / 耐電強(qiáng)度，在油中，3.2mm | 17 | kV/mm | IEC 60243-1 | |
| FLAME CHARACTERISTICS 火焰特性 | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) / UL認(rèn)可，94HB 阻燃等級(jí)(3) | 1.5 | mm | UL 94 | |
| UL Recognized, 94HB Flame Class Rating 2nd value (3) | 3 | mm | UL 94 | |
| Source GMD, last updated:11/19/2004 |
| Processing |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature / 干燥溫度 | 95 - 105 | °C |
| Drying Time / 干燥時(shí)間 | 2 - 4 | hrs |
| Maximum Moisture Content / 大含濕量 | 0.02 | % |
| Melt Temperature / 熔體溫度 | 260 - 290 | °C |
| Nozzle Temperature / 注嘴溫度 | 240 - 280 | °C |
| Front - Zone 3 Temperature / 前區(qū)3溫度 | 250 - 290 | °C |
| Middle - Zone 2 Temperature / 中區(qū)2溫度 | 250 - 290 | °C |
| Rear - Zone 1 Temperature / 后區(qū)1溫度 | 230 - 260 | °C |
| Hopper Temperature / 料筒溫度 | 60 - 80 | °C |
| Mold Temperature / 模具溫度 | 60 - 90 | °C |