LNP™STAT-KON™Compound Cycoloy_JK800

SI

|British

|Metric

|PDF

Americas: COMMERCIAL

LNP* Stat-kon* Cycoloy_JK800 compound is an 8% carbon fiber reinforcedPC+ABS, electrostatic dissipative ECO conforming FR. Good hydrolytic stability.

Property

MECHANICAL

Tensile Stress, yld, Type I, 5 mm/min

980

kgf/cm2

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min

980

kgf/cm2

ASTM D 638

Tensile Strain, yld, Type I, 5 mm/min

1.9

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

1.9

%

ASTM D 638

Tensile Modulus, 5 mm/min

77300

kgf/cm2

ASTM D 638

Flexural Stress, brk, 1.3 mm/min, 50 mm span

1470

kgf/cm2

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

63200

kgf/cm2

ASTM D 790

Tensile Stress, yield, 5 mm/min

95

MPa

ISO 527

Tensile Stress, break, 5 mm/min

95

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

1.9

%

ISO 527

Tensile Strain, break, 5 mm/min

1.9

%

ISO 527

Tensile Modulus, 1 mm/min

7500

MPa

ISO 527

Flexural Stress, yield, 2 mm/min

145

MPa

ISO 178

Flexural Stress, break, 2 mm/min

145

MPa

ISO 178

Flexural Modulus, 2 mm/min

6380

MPa

ISO 178

IMPACT

Izod Impact, unnotched, 23°C

35

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

3

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy, 23°C

841

cm-kgf

ASTM D 3763

Izod Impact, unnotched 80*10*4 +23°C

21

kJ/m2

ISO 180/1U

Izod Impact, notched 80*10*4 +23°C

4

kJ/m2

ISO 180/1A

THERMAL

Vicat Softening Temp, Rate B/50

111

°C

ASTM D 1525

HDT, 0.45 MPa, 3.2 mm, unannealed

97

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed

92

°C

ASTM D 648

HDT, 1.82 MPa, 6.4 mm, unannealed

94

°C

ASTM D 648

CTE, -40°C to 40°C, flow

2.52E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

6.48E-05

1/°C

ASTM E 831

CTE, 23°C to 80°C, flow

2.6E-05

1/°C

ISO 11359-2

CTE, 23°C to 80°C, xflow

7.4E-05

1/°C

ISO 11359-2

Vicat Softening Temp, Rate B/120

101

°C

ISO 306

Relative Temp Index, Elec

60

°C

UL 746B

Relative Temp Index, Mech w/impact

60

°C

UL 746B

Relative Temp Index, Mech w/o impact

60

°C

UL 746B

PHYSICAL

Specific Gravity

1.25

-

ASTM D 792

Mold Shrinkage, flow, 3.2 mm (5)

0.1 - 0.2

%

SABIC Method

Mold Shrinkage, xflow, 3.2 mm (5)

0.2 - 0.4

%

SABIC Method

Melt Flow Rate, 260°C/2.16 kgf

17

g/10 min

ASTM D 1238

ELECTRICAL

Volume Resistivity

1.E+03

Ohm-cm

ASTM D 257

Surface Resistivity

1.E+06

Ohm

ASTM D 257

Static Decay, 5000V to <50V

0.01

< seconds

FTMS101B

FLAME CHARACTERISTICS

UL Recognized, 94V-0 Flame Class Rating (3)

0.99

mm

UL 94

UL Recognized, 94-5VB Rating (3)

1.49

mm

UL 94

Source GMD, last updated:2002/10/29

Processing

Injection Molding

Drying Temperature

75 - 80

°C

Drying Time

3 - 4

hrs

Drying Time (Cumulative)

8

hrs

Maximum Moisture Content

0.04

%

Melt Temperature

230 - 275

°C

Nozzle Temperature

230 - 275

°C

Front - Zone 3 Temperature

225 - 275

°C

Middle - Zone 2 Temperature

215 - 260

°C

Rear - Zone 1 Temperature

210 - 255

°C

Mold Temperature

50 - 70

°C

Back Pressure

0.3 - 0.7

MPa

Screw Speed

40 - 70

rpm

Shot to Cylinder Size

30 - 80

%

Vent Depth

0.038 - 0.076

mm