LNP™STAT-KON™Compound DX07323

SI

|British

|Metric

|PDF

Americas: COMMERCIAL

LNP* STAT-KON* DX07323 is a compound based on polycarbonate resin containing conductive fillers. Added features of this compound includes: ESD safe and excellent low-temperature impact performance, intended for compliance to ATEX.

Property

MECHANICAL

Tensile Stress, yield

450

kgf/cm2

ASTM D 638

Tensile Stress, break

560

kgf/cm2

ASTM D 638

Tensile Strain, yield

5

%

ASTM D 638

Tensile Strain, break

9

%

ASTM D 638

Tensile Modulus, 5 mm/min

24400

kgf/cm2

ASTM D 638

Flexural Stress

850

kgf/cm2

ASTM D 790

Flexural Modulus

22400

kgf/cm2

ASTM D 790

Tensile Stress, yield, 5 mm/min

55

MPa

ISO 527

Tensile Stress, break, 5 mm/min

44

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

5

%

ISO 527

Tensile Strain, break, 5 mm/min

9

%

ISO 527

Tensile Modulus, 1 mm/min

2400

MPa

ISO 527

Flexural Stress, break, 2 mm/min

88

MPa

ISO 178

Flexural Modulus, 2 mm/min

2400

MPa

ISO 178

IMPACT

Izod Impact, unnotched, 23°C

163

cm-kgf/cm

ASTM D 4812

Izod Impact, unnotched, -40°C

152

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

18

cm-kgf/cm

ASTM D 256

Izod Impact, notched, -40°C

10

cm-kgf/cm

ASTM D 256

Izod Impact, unnotched 80*10*4 +23°C

130

kJ/m2

ISO 180/1U

Izod Impact, unnotched 80*10*4 -40°C

100

kJ/m2

ISO 180/1U

Izod Impact, notched 80*10*4 +23°C

16

kJ/m2

ISO 180/1A

Izod Impact, notched 80*10*4 -40°C

10

kJ/m2

ISO 180/1A

THERMAL

HDT, 1.82 MPa, 3.2mm, unannealed

125

°C

ASTM D 648

CTE, -40°C to 40°C, flow

5.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, xflow

5.E-05

1/°C

ASTM E 831

CTE, -40°C to 40°C, flow

5.E-05

1/°C

ISO 11359-2

CTE, -40°C to 40°C, xflow

5.E-05

1/°C

ISO 11359-2

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

124

°C

ISO 75/Af

PHYSICAL

Density

1.26

g/cm3

ASTM D 792

Mold Shrinkage, flow (5)

0.5

%

SABIC Method

Mold Shrinkage, xflow (5)

0.5

%

SABIC Method

Mold Shrinkage, flow, 24 hrs (5)

0.4 - 0.7

%

ASTM D 955

Mold Shrinkage, xflow, 24 hrs (5)

0.4 - 0.7

%

ASTM D 955

Melt Flow Rate, 300°C/10 kgf

55

g/10 min

ASTM D 1238

Density

1.26

g/cm3

ISO 1183

Melt Volume Rate, MVR at 300°C/10.0 kg

50

cm3/10 min

ISO 1133

ELECTRICAL

Volume Resistivity

1.E+06 - 1.E+10

Ohm-cm

ASTM D 257

Surface Resistivity

1.E+06 - 1.E+10

Ohm

ASTM D 257

FLAME CHARACTERISTICS

UL Recognized, 94V-1 Flame Class Rating (3)

2.5

mm

UL 94

Source GMD, last updated:2008/11/18

Processing

Injection Molding

Drying Temperature

120

°C

Drying Time

4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

305 - 325

°C

Front - Zone 3 Temperature

320 - 330

°C

Middle - Zone 2 Temperature

310 - 320

°C

Rear - Zone 1 Temperature

295 - 305

°C

Mold Temperature

80 - 110

°C

Back Pressure

0.2 - 0.3

MPa

Screw Speed

30 - 60

rpm